LPCB-EL-23503

Material Type 材料类型: >

LPCB-EL-23503 flame-retardant film is a clear, thin-gauge polycarbonate film with polished surfaces on both sides, and a UL94 V-0 listing to meet the stringent requirements in a wide range of electrical, electronic and transportation applications. LPCB-EL-23503 film offers ease of thermoforming, hydroforming, embossing, die-cutting, folding and bending and is very suitable for applications such as printed circuit board insulation, backlit aircraft in-flight panels and displays, business equipment insulation, computer rack partition and TV and monitor insulation.
LPCB-EL-23503阻燃薄膜是一种双面抛光、薄规格的透明聚碳酸酯薄膜，拥有 UL94 V-0 阻燃等级，能够满足广泛的电气、电子和交通应用的严格要求。该薄膜易于热成型、液压成型、压花、模切、折叠和弯曲，非常适合印刷电路板绝缘、飞机背光仪表板和显示器、办公设备绝缘、计算机机架隔板以及电视和显示器绝缘等应用。
LPCB-EL-23503_1

Specifications (Technical Performance)

 

Flammability: UL94 (V-0)
Thermal Conductivity: 0.2 W/m.K
Test Method: ASTM D5470
Dielectric Constant: 2.9 (60Hz) , 2.8 (1MHz)
Test Method: ASTM D150
Dielectric Strength: 59.0kV/mm
Volume Resistivity: 10 ^ 17 Ω.cm
Test Method: ASTM D257
Surface Resistivity: 10 ^ 16 Ω/sq
Test Method: ASTM D257
Density/Specific Gravity
(Foam/Sponge):		 1344.00 kg/m³
Test Method: ISO 1183
Heat Capacity: 1.25 kJ/kg.˚C
Test Method: ASTM E1269
Water Absorption: 0.28%
Test Method: ISO 62
Linear Shrinkage: 0.09%
Test Method: ASTM D1204
Vicat Softening Temperature: 141˚C
Test Method: ASTM 1525
Elongation: 100%
Test Method: ISO 527
Tear Strength: 298.0 kN/m
Test Method: ASTM D1004
Tensile Strength: 65.0 MPa (Yield) – 70.0 MPa (Ultimate)
Test Method: ISO 527
Modulus: 2200.0 Mpa
Test Method: ISO 527

规格（技术性能）

 

阻燃等级： UL94 (V-0)
导热系数： 0.2 W/m·K
测试方法：ASTM D5470
介电常数： 2.9 (60Hz) / 2.8 (1MHz)
测试方法：ASTM D150
介电强度： 59.0 kV/mm
体积电阻率： 10¹⁷ Ω·cm
测试方法：ASTM D257
表面电阻率： 10¹⁶ Ω/sq
测试方法：ASTM D257
密度/比重
（泡绵/海绵）：		 1344.00 kg/m³
测试方法：ISO 1183
比热容： 1.25 kJ/kg·°C
测试方法：ASTM E1269
吸水率： 0.28%
测试方法：ISO 62
线性收缩率： 0.09%
测试方法：ASTM D1204
维卡软化温度： 141°C
测试方法：ASTM D1525
伸长率： > 100%
测试方法：ISO 527
撕裂强度： 298.0 kN/m
测试方法：ASTM D1004
拉伸强度： 65.0 MPa (屈服) – 70.0 MPa (极限)
测试方法：ISO 527
拉伸模量： >2200.0 MPa
测试方法：ISO 527
Back to previous page 返回上一页